Show simple item record

dc.contributor.authorMollah, M. Z. I.
dc.contributor.authorRahaman, M S.
dc.contributor.authorFaruque, M R I.
dc.contributor.authorKhandaker, M. U.
dc.contributor.authorOsman, Hamid
dc.contributor.authorAlamri, Sultan
dc.contributor.authorAl-Assaf, Saphwan
dc.date.accessioned2022-01-04T13:27:26Z
dc.date.available2022-01-04T13:27:26Z
dc.date.issued2021-12-20
dc.date.submitted2021-08-20
dc.identifierhttps://chesterrep.openrepository.com/bitstream/handle/10034/626612/fmats-08-761995.pdf?sequence=2
dc.identifier.citationMollah, M. Z. I., Rahaman, M S., Faruque, M R I., Khandaker, M. U., Osman, H., Alamri, S., & Al-Assaf, S. (2021). Effects of radiation sterilization dose on the molecular weight and gelling properties of commercial alginate samples. Frontiers in Materials, 8, 761995. https://doi.org/10.3389/fmats.2021.761995
dc.identifier.urihttp://hdl.handle.net/10034/626612
dc.descriptionFrom Frontiers via Jisc Publications Router
dc.descriptionHistory: collection 2021, received 2021-08-20, accepted 2021-11-12, epub 2021-12-20
dc.descriptionPublication status: Published
dc.description.abstractTo estimate the molecular weight (Mw) and gelling properties, a total of 26 alginate samples consisting of control (n = 13) and 15 kGy γ-irradiated (n = 13) samples were characterized through viscometric and gel permeation chromatography (GPC-MALLS) methods. Based on the observations, a remarkable decrease in the intrinsic viscosity of all samples of alginates was evident due to the effects of radiation, with a linear relationship between viscosity and concentration in 0.01 M NaCl solution. The correlation among the Mw, percentage mass recovery, radii of gyration (Rz/Rg), and percentage reduction of Mw assessed by GPC was significant. The Mw decreased dramatically (from 3.1 × 105 to 0.49 × 105 mole/g in sample no. 12) by the effect of radiation with momentous relation to the % reduction of the molecular weight. The highest molecular weight reduction (84%), which is the most sensitive to γ-radiation, and the average reduction rate was ≥50%. The mass recovery was 100% obtained from samples no. 1,3,4,5,7,12, and 13, while the rest of the samples’ recovery rate was significantly higher. The reduction rate of mass molecular weight (Mw) is higher than the average molecular weight (Mv), but they showed a sensitivity towards radiation, consequently their performance are different from each other. The stability test was performed as a critical behaviour in the control, recurrently same as in the irradiated samples. Thus, the sterilization dose of 15 kGy for the Mw distribution, and subsequently for the characterization, was significantly effective.
dc.languageen
dc.publisherFrontiers Media S.A.
dc.relation.urlhttps://www.frontiersin.org/articles/10.3389/fmats.2021.761995/full
dc.rightsLicence for this article: http://creativecommons.org/licenses/by/4.0/
dc.rights.urihttps://creativecommons.org/licenses/by/4.0/
dc.sourceeissn: 2296-8016
dc.subjectMaterials
dc.subjectalginate (ALG)
dc.subjectirradiation
dc.subjectmolecular weight (Mw)
dc.subjectreduction
dc.subjectsterilization
dc.subjectcharacterization
dc.titleEffects of Radiation sterilization Dose on the Molecular Weight and Gelling Properties of Commercial Alginate Samples
dc.typearticle
dc.contributor.departmentUniversiti Kebangsaan Malaysia; Bangladesh Atomic Energy Commission; Sunway University; Taif University; University of Chester
dc.date.updated2022-01-04T13:27:25Z
dc.date.accepted2021-11-12


Files in this item

Thumbnail
Name:
fmats-08-761995.pdf
Size:
1.615Mb
Format:
PDF

This item appears in the following Collection(s)

Show simple item record

Licence for this article: http://creativecommons.org/licenses/by/4.0/
Except where otherwise noted, this item's license is described as Licence for this article: http://creativecommons.org/licenses/by/4.0/