• Effects of inkjet printed toughener on delamination suppression in drilling of carbon fibre reinforced plastics (CFRPs)

      Shi, Yu; Wang, Xiaonan; Wang, Fuji; Gu, Tianyu; Xie, Pengheng; Jia, Yu; University of Chester; Dalian University of Technology; Aston University
      Delamination has been recognised as the predominant damage induced during the drilling of carbon fibre reinforced plastics (CFRPs). It could significantly reduce the bearing capacity and shorten the service life of the designed component. To enhance the delamination resistance of CFRPs for different applications, great affords have been done to improve their interlaminar fracture toughness. However, due to the difficulty in accurately controlling the amount of the toughener applied in the interface, effect of the toughener content on the toughening efficiency is rarely studied. In this work, an experimental research was developed to investigate the performance of the toughener on the improvement of delamination resistance in the drilling of CFRPs and parametrically optimise the toughener content with the consideration of different feed rates. Specifically, poly(methyl methacrylate) (PMMA) solutions with various concentrations were selected to add on the CFRP prepreg, and co-cured together with layups. The inkjet printing technology was adopted to deposit the PMMA solutions for precisely controlled toughener contents. Through drilling experiments on the toughened CFRPs, it was found that the optimal content of the PMMA solution was 10 wt% to offer the least delamination, in particular, for the situation under the highest feed rate condition. The toughing mechanisms were also concluded by analysing the histories of the thrust force and torque in the drilling process. The results of this study is significantly contribute to the locally toughening of the composite interfaces and the improvement of the drilling quality, which is specifically helpful to strengthen the joint property for the structural design stage for the aircraft.
    • Modelling impact damage in composite laminates: A simulation of intra- and inter-laminar cracking

      Pinna, Christophe; Soutis, Constantinos; Shi, Yu; University of Chester; University of Sheffield; University of Manchester (Elsevier, 2014-04-12)
      In this work, stress- and fracture mechanics-based criteria are developed to predict initiation and evolution, respectively, of intra- and inter-laminar cracking developed in composite laminates subjected to a relatively low energy impact (⩽15 J) with consideration of nonlinear shear behaviour. The damage model was implemented in the finite element (FE) code (Abaqus/Explicit) through a user-defined material subroutine (VUMAT). Delamination (or inter-laminar cracking) was modelled using interface cohesive elements while splitting and transverse matrix cracks (intralaminar cracking) that appeared within individual plies were also simulated by inserting cohesive elements along the fibre direction (at a crack spacing determined from experiments for computing efficiency). A good agreement is obtained when the numerically predicted results are compared to both experimentally obtained curves of impact force and absorbed energy versus time and X-ray radiography damage images, provided the interface element stiffness is carefully selected. This gives confidence to selected fracture criteria and assists to identify material fracture parameters that influence damage resistance of modern composite material systems.