• High speed CO2 laser surface modification of iron/cobalt co-doped boroaluminosilicate glass

      Hodgson, Simon D.; Waugh, David G.; Gillett, Alice R.; Lawrence, Jonathan; University of Chester (IOP Publishing, 2016-06-10)
      A preliminary study into the impact of high speed laser processing on the surface of iron and cobalt co-doped glass substrates using a 60 W continuous wave (cw) CO2 laser. Two types of processing, termed fill-processing and line-processing, were trialled. In fill-processed samples the surface roughness of the glass was found to increase linearly with laser power from an Sa value of 20.8 nm–2.1 μm at a processing power of 54 W. With line processing, a more exponential-like increase was observed with a roughness of 4 μm at 54 W. The change in surface properties of the glass, such as gloss and wettability, have also been measured. The contact angle of water was found to increase after laser processing by up to 64°. The surface gloss was varied between 45 and 100 gloss units (GUs).
    • On the study of oil paint adhesion on optically transparent glass: Conservation of reverse paintings on glass

      Bayle, M.; Waugh, David G.; Colston, Belinda J.; Lawrence, Jonathan; University of Chester (Elsevier, 2015-12-01)
      Reverse painting on glass is a technique which consists of applying a cold paint layer on the reverse-side of glass. The main challenge facing these artworks is the fragile adhesion of the pictorial layer – a simple movement can modify the appearance of the painting. This paper details a study into the adhesion parameters of pigments on glass and the comparison between different pigments. The relationships between the binder (linseed oil) with pigments and the glass with or without the use of an adhesive are studied. Physical analyses by surface characterisation have been carried out to better understand the influence of the pigment. The use of a sessile drop device, optical microscopy, scanning electron microscopy (SEM), a surface 3D profiler and a pencil hardness scratch tester were necessary to establish a comparison of the pictorial layer adhesion. A comparison of the effect of two adhesives; namely ox gall and gum arabic, has shown that the adhesion is not only linked to the physical parameters but that possible chemical reactions can influence the results. Finally, a treatment based on humidity-extreme storage has shown the weakness of some pictorial layers.