• Computational simulation of the damage response for machining long fibre reinforced plastic (LFRP) composite parts: A review

      Wang, Xiaonan; Wang, Fuji; Gu, Tianyu; Jia, Zhenyuan; Shi, Yu; Dalian University of Technology; University of Chester
      Long fibre reinforced plastics (LFRPs) possess excellent mechanical properties and are widely used in the aerospace, transportation and energy sectors. However, their anisotropic and inhomogeneous characteristics as well as their low thermal conductivity and specific heat capacity make them prone to subsurface damage, delamination and thermal damage during the machining process, which seriously reduces the bearing capacity and shortens the service life of the components. To improve the processing quality of composites, finite element (FE) models were developed to investigate the material removal mechanism and to analyse the influence of the processing parameters on the damage. A review of current studies on composite processing modelling could significantly help researchers to understand failure initiation and development during machining and thus inspire scholars to develop new models with high prediction accuracy and computational efficiency as well as a wide range of applications. To this aim, this review paper summarises the development of LFRP machining simulations reported in the literature and the factors that can be considered in model improvement. Specifically, the existing numerical models that simulate the mechanical and thermal behaviours of LFRPs and LFRP-metal stacks in orthogonal cutting, drilling and milling are analysed. The material models used to characterise the constituent phases of the LFRP parts are reviewed. The mechanism of material removal and the damage responses during the machining of LFRP laminates under different tool geometries and processing parameters are discussed. In addition, novel and objective evaluations that concern the current simulation studies are conducted to summarise their advantages. Aspects that could be improved are further detailed, to provide suggestions for future research relating to the simulation of LFRP machining.
    • Effects of inkjet printed toughener on delamination suppression in drilling of carbon fibre reinforced plastics (CFRPs)

      Shi, Yu; Wang, Xiaonan; Wang, Fuji; Gu, Tianyu; Xie, Pengheng; Jia, Yu; University of Chester; Dalian University of Technology; Aston University
      Delamination has been recognised as the predominant damage induced during the drilling of carbon fibre reinforced plastics (CFRPs). It could significantly reduce the bearing capacity and shorten the service life of the designed component. To enhance the delamination resistance of CFRPs for different applications, great affords have been done to improve their interlaminar fracture toughness. However, due to the difficulty in accurately controlling the amount of the toughener applied in the interface, effect of the toughener content on the toughening efficiency is rarely studied. In this work, an experimental research was developed to investigate the performance of the toughener on the improvement of delamination resistance in the drilling of CFRPs and parametrically optimise the toughener content with the consideration of different feed rates. Specifically, poly(methyl methacrylate) (PMMA) solutions with various concentrations were selected to add on the CFRP prepreg, and co-cured together with layups. The inkjet printing technology was adopted to deposit the PMMA solutions for precisely controlled toughener contents. Through drilling experiments on the toughened CFRPs, it was found that the optimal content of the PMMA solution was 10 wt% to offer the least delamination, in particular, for the situation under the highest feed rate condition. The toughing mechanisms were also concluded by analysing the histories of the thrust force and torque in the drilling process. The results of this study is significantly contribute to the locally toughening of the composite interfaces and the improvement of the drilling quality, which is specifically helpful to strengthen the joint property for the structural design stage for the aircraft.