• Perovskite Srx(Bi1-xNa0.97-xLi0.03)0.5TiO3 ceramics with polar nano regions for high power energy storage

      Wu, Jiyue; Mahajan, Amit; Riekehr, Lars; Zhang, Hangfeng; Yang, Bin; Meng, Nan; Zhang, Zhen; Yan, Haixue; Queen Mary University of London; Uppsala University; University of Chester (Elsevier, 2018-06-06)
      Dielectric capacitors are very attractive for high power energy storage. However, the low energy density of these capacitors, which is mainly limited by the dielectric materials, is still the bottleneck for their applications. In this work, lead-free single-phase perovskite Srx(Bi1-xNa0.97-xLi0.03)0.5TiO3 (x=0.30 and 0.38) bulk ceramics, prepared using solid-state reaction method, were carefully studied for the dielectric capacitor application. Polar nano regions (PNRs) were created in this material using co-substitution at A-site to enable relaxor behaviour with low remnant polarization (Pr) and high maximum polarization (Pmax). Moreover, Pmax was further increased due to reversible electric field induced phase transitions. Comprehensive structural and electrical studies were performed to confirm the PNRs and the reversible phase transitions. And finally a high energy density (1.70 J/cm3) with an excellent efficiency (87.2%) was achieved using the contribution of PNRs and field-induced transitions in this material, making it among the best performing lead-free dielectric ceramic bulk material for high energy storage.